The high-tech material
FAB Titanium G5 – titanium for the dental technology
For consistent quality results. With the titanium blank FAB Titanium G5, dental laboratories can achieve thin-walled frameworks thanks to a minimum edge thickness of just 0.10 mm.
According to type 4 EN ISO 22674:2016, the dental alloy FAB Titanium G5 stands for maximum biocompatibility due to the high corrosion resistance of the material. For precisely fitting abutments and tension-free bar works. Ideal up to 16 units.
Composition: Ti 90 %, Al 6 %, V: 4 %, traces of Fe
Titanium blank FAB Titanium G5 – high-tech material for high wearing comfort.
FAB Titanium G5 is a dental metal alloy in form of titanium blank. Due to its low weight, this light metal offers a high level of wearing comfort, especially when working with large spans. With a CTE value (20-600 °C) of 10*10-6K-1, the alpha-case-free titanium blank FAB Titanium G5 can be reliably veneered. Dental laboratories cover all allergy-friendly indications with this high-tech CAD/CAM material.
FAB Titanium G5
Density: 4,4 g/cm3
Vickers hardness: 312 HV 10
Modulus of elasticity: 114 GPa
CTE(20-600 °C): 110*10-6K-1
Tensile strength: ≥ 880 MPa
Blank height: 10, 12, 13,5, 15, 18 and 20 mm
FAB Zirconia ST
Festigkeit: 1050 MPa
Transluzenz: 47–49 %
Farbverlauf: nein
WAK: (10,5 ± 0,5) *10-6*K-1
Farben: 16 Farben
Rondenhöhe: 14, 16, 18, 20 und 25 mm
FAB Zirconia ML
Festigkeit: 1050 MPa
Transluzenz: 47–49 %
Farbverlauf: ja
WAK: (10,5 ± 0,5) *10-6*K-1
Farben: 16 Farben
Rondenhöhe: 14, 18, 20 und 25 mm
FAB Zirconia HT
Festigkeit: 1050 MPa
Transluzenz: 41–43 %
Farbverlauf: nein
WAK: (10,5 ± 0,5) *10-6*K-1
Farben: weiß für die Infiltrationstechnik
Rondenhöhe: 14, 16, 18, 20 und 25 mm
The high-tech material titanium grad 5
Highly stable, biocompatible and light as a feather. Perfect for solid bridges with up to 16 units, tension-free bar works and precisely fitting abutments.